           35
   Defect C_si  
   C     0.000000    0.000000    0.000000
   C     1.071320    1.071563    1.071641
   Si    2.142561    2.142572    0.000633
   Si    0.000022    2.143182    2.143202
   Si    2.142697    0.000496    2.142728
   Si    0.000158    0.001107    4.285297
   Si   -0.000158   -0.001107   -4.285297
   C     1.071162    1.070456   -3.213656
   Si   -0.000136    2.142075   -2.142095
   C     1.071184    3.213638   -1.070454
   Si    2.142539   -0.000611   -2.142569
   C     3.213860    1.070952   -1.070929
   Si   -0.000114    4.285257    0.001107
   Si    0.000114   -4.285257   -0.001107
   C     1.071434   -3.213695    1.070534
   Si    2.142676   -2.142685   -0.000474
   C     3.213996   -1.071123    1.071166
   Si    0.000136   -2.142075    2.142095
   C     1.071456   -1.070512    3.213736
   Si   -0.000022   -2.143182   -2.143202
   C     1.071298   -1.071619   -1.071561
   Si    4.285237   -0.000114    0.000158
   Si   -4.285236    0.000114   -0.000158
   C    -3.213916    1.071677    1.071482
   Si   -2.142675    2.142686    0.000474
   C    -1.071355    3.214248    1.072115
   Si   -2.142539    0.000611    2.142570
   C    -1.071219    1.072173    3.214210
   Si   -2.142697   -0.000496   -2.142727
   C    -1.071377    1.071066   -1.071087
   Si   -2.142561   -2.142571   -0.000633
   C    -1.071241   -1.071009    1.071008
   C    -1.071399   -1.072116   -3.214289
   C    -3.213938   -1.071505   -1.071719
   C    -1.071263   -3.214191   -1.072194